BETTERCOAT ® SL 704-SS
Epoxy Mortar SL 704-SS
Description A two packs polyamide cured epoxy resin based.
Use Bettecoat SL704-SS is a two-component epoxy backing compound specifically designed for various mining and quarrying applications. It serves as a backing and reinforcing layer between machine parts and as a damper when subjected to impact and shock loads
Features Super corrosion resistance and adhesion.
Excellent chemical resistance, water and salt water resistant
Excellent water resistance and very high compressive strength
Ligh grey
Glossy
Technical Data Packing: 5 kgs/set vaø 20 kgs/set
No. of components: two
Viscosity (28 oC) : approx 140KU
Mixing ratio: 160 (base) 60 (Hard) by weight
Pot life (28 oC) : 30 mins
Solid conent: 100%
Specific gravity: Approx. 1.50
Flash point : 24 oC
Application data Application method : Trowel tool
Thinner: useless
Shelf life : 12 months
Spreading rate : 4 m2/kg/coat
Dry film thickness: 200μm/coat
Drying time: touch dry : 5 hours at 28 oC
Hard dry: 24 hours at 28 oC
Recoating interval: Min 12 hours , Max 1 month at ôû 28 oC
Painting specification Surface preparation: Ensure a clean dry for general usage, such as tie coats.
Storage : cool, dry, well ventilated shaded areas .
Safety precaution No excessive heat, sparks or flame.
Use adequate ventilation. Avoid prolong contract with skin. Avoid breathing of vapor and spray mist. Use protective equipment. If the material comes in contract with the eye, immediately wash in running water for 20 minutes and obtain medical treatment. Observe all safe precautions.
Test standard Compressive strength 80.00N/mm2 ASTM C579
Tensile strength 25.00N/mm2 ASTM C367
Water permeability Less than 1.0mm JIS K5400
Impact resistance 1/4’’ x 500g x 30 cm JIS K5400
Hardness 2H JIS K5400
Adhesion (Cross cut) 100/100 JIS K5400